ANSI/AWS C3.7:2005

This specification presents minimum fabrication, equipment, material, process procedure requirements and inspection requirements for the brazing of aluminum by all the processes commonly used; atmosphere furnace, vacuum furnace, and flux processes. Its purpose is to standardize aluminum brazing requirements for all applications where brazed joints based on loading and the consequences of failure and quality assurance criteria defining the limits of acceptibility of each class. The specification defines acceptable brazing equipment, materials and procedures as well as required inspection for each class of joint.



Keywords: AWS C3.7-05; AWS C3.7-2005

This product references:ANSI/AWS A2.4:2007 - Standard Symbols for Welding, Brazing, Nondestructive Examination
ANSI/AWS A5.8/A5.8M:2004 - Specification for Filler Metals for Brazing and Braze Welding
ANSI/AWS A5.31-92 - Specification for Fluxes for Brazing and Braze Welding
ANSI/AWS B2.2-91 - Standard for Brazing Procedure and Performance Qualification
ANSI/AWS C3.3:2008 - Recommended Practices for Design, Manufacture, and Inspection of Critical Brazed Components
ANSI/AWS C3.8M/C3.8:2005 - Specification for the Ultrasonic Examination of Brazed Joints
ANSI/NCSL Z540.3-2006 - Requirements for the Calibration of Measuring and Test Equipment
ASTM E230-03 - Standard Specification and Temperature-Electromotive Force (EMF) Tables for Standardized Thermocouples
ASTM E1417-05e1 - Standard Practice for Liquid Penetrant Testing
ASTM E1742-08 - Standard Practice for Radiographic Examination
ANSI/ASQ Z1.4-2003 - Sampling Procedures and Tables for Inspection by Attributes
SAE AMS 2750D - Pyrometry ( Reaffirmed: Apr 1994 )
This product is related to: ANSI/AWS C3.9/C3.9M:2009 - Specification for Aluminum Brazing

People Who Bought This Also Bought:
ANSI/AWS C3.6M/C3.6:2008- Specification for Furnace BrazingANSI/AWS C3.5M/C3.5:2007- Specification for Induction BrazingANSI/AWS C3.4M/C3.4:2007- Specification for Torch BrazingSAE AMS 4766G- Silver Alloy, Brazing Filler Metal 85Ag 15Mn, 1760 to 1780 mDF (960 to 971mDC) Solidus-Liquidus Range ( Reaffirmed: Apr 2006 Jun 2009 )ANSI/AWS A2.4:2007- Standard Symbols for Welding, Brazing, Nondestructive ExaminationANSI/AWS C3.8M/C3.8:2005- Specification for the Ultrasonic Examination of Brazed JointsASTM E139-06- Standard Test Methods for Conducting Creep, Creep-Rupture, and Stress-Rupture Tests of Metallic MaterialsASTM D1002-05- Standard Test Method for Apparent Shear Strength of Single-Lap-Joint Adhesively Bonded Metal Specimens by Tension Loading (Metal-to-Metal)SAE AMS 2816W- Identification Welding Wire, Tab Marking MethodANSI/ASME Y14.5M-1994 (R2004)- Dimensioning and Tolerancing